Nanostructured conducting polymer composites

Minisy, Islam

Nanostrukturované vodivé polymerní kompozity

dc.contributor.advisor	Bober, Patrycja Magdalena
dc.creator	Minisy, Islam
dc.date.accessioned	2022-05-26T12:34:51Z
dc.date.available	2022-05-26T12:34:51Z
dc.date.issued	2022
dc.identifier.uri	http://hdl.handle.net/20.500.11956/172444
dc.description.abstract	Conducting polymers (CPs) combine the electrical properties of semiconductors and material properties of organic polymers. Polypyrrole (PPy) and polyaniline (PANI) are the most studied CPs due to their relatively high electrical conductivity (typically several units S cm-1 ), environmental stability, ease of preparation, good processability and low cost. Organic dyes have similar properties as surfactants, with an interesting ability to form various organized templates in water that could during synthesis tailor PPy morphologies to various nanostructures with high yield and improved electrical conductivity. Herein, PPy was prepared in the presence of cations dyes, safranin and phenosafranin, and anionic dye, methyl red, to obtain various nanostructures. The effect of dye concentration, oxidant-to-pyrrole mole ratio and other polymerization conditions on the physicochemical properties of the produced PPy was carefully investigated. Pyrrole was polymerized in the frozen reaction media at −24 řC in the presence of safranin, Acid Blue 25 (AB) or methyl orange (MO). Prepared one-dimensional nanostructures exhibited high yield and improved conductivity; the highest conductivity of 175 S cm−1 was obtained when safranin was used. Polypyrrole nanotubes prepared in the presence of MO were carbonized at 650...	en_US
dc.description.abstract	Vodivé polymery kombinují elektrické vlastnosti polovodičů s materiálovými vlastnostmi organických polymerů. Polypyrrol (PPy) a polyanilin (PANI) jsou nejvíce studovanými polymery díky relativně vysoké elektrické vodivosti (několik jednotek S cm−1 ), dobré stabilitě v běžném prostředí, jednoduchosti přípravy, dobré zpracovatelnosti a nízké ceně. Organická barviva mají podobné vlastnosti jako surfaktanty se zajímavou schopností vytváření různých organizovaných struktur ve vodě, které mohou při přípravě upravovat morfologii PPy do různých nanostruktur, a to ve vysokém výtěžku a se zlepšenou vodivostí. V této práci, PPy byl připraven v přítomnosti kationtových barviv, safraninu a fenosafraninu, a aniontového barviva, methylčerveně, s cílem získat různé nanostruktury. Byl pečlivě zkoumám vliv koncentrace barviva a molárního poměru oxidant/pyrrol na fyzikálně chemické vlastnosti vytvářeného PPy. Pyrrol byl polymerován ve zmrzlém reakčním mediu při −24 řC v přítomnosti safraninu, Acid Blue 25, a methyloranže. Přípravené jednorozměrné nanostruktury vykázaly vysoký výtěžek a zlepšenou vodivost, kdy nejvyšší vodivost 175 S cm−1 byla získána při použití safraninu. Polypyrrolové nanotrubky připravené v přítomnosti methyloranže byly karbonizovány při 650řC v inertní atmosféře a následně pokryty polypyrrolem...	cs_CZ
dc.language	English	cs_CZ
dc.language.iso	en_US
dc.publisher	Univerzita Karlova, Přírodovědecká fakulta	cs_CZ
dc.subject	Conducting polymers	en_US
dc.subject	Conductivity	en_US
dc.subject	Cryopolymerization	en_US
dc.subject	Dye adsorption	en_US
dc.subject	Magnetic composites	en_US
dc.subject	Morphology	en_US
dc.subject	Organic dyes	en_US
dc.subject	Poly(p-phenylenediamine)	en_US
dc.subject	Polyaniline	en_US
dc.subject	Polymerization temperature	en_US
dc.subject	Polypyrrole	en_US
dc.subject	Vodivé polymery	cs_CZ
dc.subject	Vodivost	cs_CZ
dc.subject	Kryopolymerace	cs_CZ
dc.subject	Adsorpce barviv	cs_CZ
dc.subject	Magnetické kompozity	cs_CZ
dc.subject	Morfologie	cs_CZ
dc.subject	Organická barviva	cs_CZ
dc.subject	Poly(p-fenylendiamin)	cs_CZ
dc.subject	Polyaniline	cs_CZ
dc.subject	Polymerační teplota	cs_CZ
dc.subject	Polypyrrol	cs_CZ
dc.title	Nanostructured conducting polymer composites	en_US
dc.type	dizertační práce	cs_CZ
dcterms.created	2022
dcterms.dateAccepted	2022-04-29
dc.description.department	Katedra fyzikální a makromol. chemie	cs_CZ
dc.description.department	Department of Physical and Macromolecular Chemistry	en_US
dc.description.faculty	Faculty of Science	en_US
dc.description.faculty	Přírodovědecká fakulta	cs_CZ
dc.identifier.repId	196384
dc.title.translated	Nanostrukturované vodivé polymerní kompozity	cs_CZ
dc.contributor.referee	Kovalčík, Adriána
dc.contributor.referee	Lisak, Grzegorz
thesis.degree.name	Ph.D.
thesis.degree.level	doktorské	cs_CZ
thesis.degree.discipline	Macromolecular Chemistry	en_US
thesis.degree.discipline	Makromolekulární chemie	cs_CZ
thesis.degree.program	Macromolecular Chemistry	en_US
thesis.degree.program	Makromolekulární chemie	cs_CZ
uk.thesis.type	dizertační práce	cs_CZ
uk.taxonomy.organization-cs	Přírodovědecká fakulta::Katedra fyzikální a makromol. chemie	cs_CZ
uk.taxonomy.organization-en	Faculty of Science::Department of Physical and Macromolecular Chemistry	en_US
uk.faculty-name.cs	Přírodovědecká fakulta	cs_CZ
uk.faculty-name.en	Faculty of Science	en_US
uk.faculty-abbr.cs	PřF	cs_CZ
uk.degree-discipline.cs	Makromolekulární chemie	cs_CZ
uk.degree-discipline.en	Macromolecular Chemistry	en_US
uk.degree-program.cs	Makromolekulární chemie	cs_CZ
uk.degree-program.en	Macromolecular Chemistry	en_US
thesis.grade.cs	Prospěl/a	cs_CZ
thesis.grade.en	Pass	en_US
uk.abstract.cs	Vodivé polymery kombinují elektrické vlastnosti polovodičů s materiálovými vlastnostmi organických polymerů. Polypyrrol (PPy) a polyanilin (PANI) jsou nejvíce studovanými polymery díky relativně vysoké elektrické vodivosti (několik jednotek S cm−1 ), dobré stabilitě v běžném prostředí, jednoduchosti přípravy, dobré zpracovatelnosti a nízké ceně. Organická barviva mají podobné vlastnosti jako surfaktanty se zajímavou schopností vytváření různých organizovaných struktur ve vodě, které mohou při přípravě upravovat morfologii PPy do různých nanostruktur, a to ve vysokém výtěžku a se zlepšenou vodivostí. V této práci, PPy byl připraven v přítomnosti kationtových barviv, safraninu a fenosafraninu, a aniontového barviva, methylčerveně, s cílem získat různé nanostruktury. Byl pečlivě zkoumám vliv koncentrace barviva a molárního poměru oxidant/pyrrol na fyzikálně chemické vlastnosti vytvářeného PPy. Pyrrol byl polymerován ve zmrzlém reakčním mediu při −24 řC v přítomnosti safraninu, Acid Blue 25, a methyloranže. Přípravené jednorozměrné nanostruktury vykázaly vysoký výtěžek a zlepšenou vodivost, kdy nejvyšší vodivost 175 S cm−1 byla získána při použití safraninu. Polypyrrolové nanotrubky připravené v přítomnosti methyloranže byly karbonizovány při 650řC v inertní atmosféře a následně pokryty polypyrrolem...	cs_CZ
uk.abstract.en	Conducting polymers (CPs) combine the electrical properties of semiconductors and material properties of organic polymers. Polypyrrole (PPy) and polyaniline (PANI) are the most studied CPs due to their relatively high electrical conductivity (typically several units S cm-1 ), environmental stability, ease of preparation, good processability and low cost. Organic dyes have similar properties as surfactants, with an interesting ability to form various organized templates in water that could during synthesis tailor PPy morphologies to various nanostructures with high yield and improved electrical conductivity. Herein, PPy was prepared in the presence of cations dyes, safranin and phenosafranin, and anionic dye, methyl red, to obtain various nanostructures. The effect of dye concentration, oxidant-to-pyrrole mole ratio and other polymerization conditions on the physicochemical properties of the produced PPy was carefully investigated. Pyrrole was polymerized in the frozen reaction media at −24 řC in the presence of safranin, Acid Blue 25 (AB) or methyl orange (MO). Prepared one-dimensional nanostructures exhibited high yield and improved conductivity; the highest conductivity of 175 S cm−1 was obtained when safranin was used. Polypyrrole nanotubes prepared in the presence of MO were carbonized at 650...	en_US
uk.file-availability	V
uk.grantor	Univerzita Karlova, Přírodovědecká fakulta, Katedra fyzikální a makromol. chemie	cs_CZ
thesis.grade.code	P
uk.publication-place	Praha	cs_CZ
uk.thesis.defenceStatus	O